Voided latex particles containing functionalized outer shells

ABSTRACT

The wet adhesion of a coating composition may be improved through the use of voided latex particles as opacifying agents which contain a hollow interior as well as an outer shell of a polymer containing functional groups such as amino, 1,3-diketo, urea or ureido. Other types of functional groups may be introduced to the outer shell polymer in order to vary other desired characteristics of the coating. The voided latex particles are non-film-forming.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a national stage application under 35 U.S.C. § 371 of PCT/US2016/44958 filed Aug. 1, 2016, which claims benefit to U.S. patent application Ser. No. 62/200697, filed Aug. 4, 2015.

TECHNICAL FIELD

The present application relates to latex particles and emulsion polymerization processes for producing such particles. In particular, the present application relates to aqueous emulsion polymerization processes for preparing “hollow” or “voided” latex particles and the latex particles prepared therefrom, which are useful as non-film-forming opacifiers.

BACKGROUND OF THE INVENTION

Paints and coatings play an important role in preserving, protecting and beautifying the objects to which they are applied. Architectural paints are used to decorate and extend the service life of the interior and exterior surfaces of residential and commercial buildings.

“Hollow latexes (i.e., voided latex particles) which are non-film-forming have been developed for use as opacifiers in paints and other coatings. As such, they are typically used as full or partial replacements for other opacifying agents such as titanium dioxide. Performance properties impacted include, but are not limited to, wet adhesion, block resistance, scrub resistance, solvent resistance and stain resistance. “Wet adhesion” refers to the level of adhesion to a substrate surface that a coating exhibits under conditions of high humidity, condensation, or precipitation. “Blocking” is said to occur when two painted surfaces adhere to each other when pressed together. “Scrub resistance” is a measure of the resistance of the paint to abrasive wear. “Solvent resistance” is a measure of the resistance of the paint to deterioration due to exposure to various organic solvents. “Stain resistance” refers to the ease with which contaminants such as lipstick, crayon, ketchup and mustard can be removed from a painted surface. Limiting the negative impact on the performance properties of coatings containing voided latex particles thus would be desirable.

SUMMARY OF THE INVENTION

The present invention provides a voided latex particle comprising a hollow interior (void) and an outer shell, wherein the outer shell is comprised of an outer shell polymer having a glass transition temperature (Tg) of at least above 45° C., or of least 50° C., or of least 60° C., and bearing functional groups. The functional groups may, for example, be selected from 1,3-diketo, amino, ureido, urea, hydroxyl, silane, phosphate, polyether, epoxy, fluorocarbon, aldehyde, ketone, acetoacetyl functional groups or combinations thereof. Such particles are non-film-forming opacifying agents which can be added to coating compositions such as paints, not only to enhance hiding but also to impart improved wet adhesion and/or block resistance and/or other characteristics.

The invention also provides a process for forming non-film-forming voided latex particles, wherein the process comprises contacting multi-stage emulsion polymer particles comprising a core and an outer shell with a swelling agent, wherein:

the core comprises a hydrophilic component such as a polymer of at least one hydrophilic monoethylenically unsaturated monomer;

the outer shell comprises an outer shell polymer having a Tg of at least above 45° C., or at least 50° C., or at least 60° C., and bearing functional groups selected from 1,3-diketo, amino, ureido, urea, hydroxyl, silane, phosphate, polyether, epoxy, fluorocarbon, aldehyde, ketone, acetoacetyl, or combinations thereof; and

the swelling agent is capable of swelling the core.

The invention additionally furnishes multi-stage emulsion polymer particles useful for forming non-film-forming voided latex particles, wherein a multi-stage emulsion polymer particle comprises a core and an outer shell. The core comprises a hydrophilic component (e.g., a polymer of at least one hydrophilic monoethylenically unsaturated monomer) and is capable of being swollen with a swelling agent. The outer shell comprises an outer shell polymer having a Tg of at least above 45° C., or at least 50° C., or at least 60° C., and bearing functional groups selected from 1,3-diketo, amino, ureido, hydroxyl, silane, phosphate, polyether, epoxy, fluorocarbon, aldehyde, ketone, acetoacetyl, or combinations thereof.

DESCRIPTION OF FIGURES

FIG. 1 illustrates in schematic form an exemplary process which can be used to obtain multi-stage emulsion polymer particles and voided latex particles in accordance with the invention.

FIG. 2 illustrates the impact of acrylic latex modification, voided latex particle opacifier level, and functionalized monomer content of the outer shells of the voided latex particles on wet adhesion to a gloss alkyd substrate, as explained in more detail in the Examples.

DETAILED DESCRIPTION OF THE INVENTION

The voided latex particles of the present invention may be characterized as being “non-film-forming.” By “non-film-forming” it is meant that the voided latex particles will not form a film at ambient temperature or below, or in other words will only form a film at temperatures above ambient temperature. For the purposes of this specification, ambient temperature is taken as being in the range of 15° C. to 45° C. Thus, for example, when incorporated into an aqueous coating composition, applied to a substrate temperature and dried or cured at ambient temperature or below, the voided latex particles do not form a film. The voided latex particles generally remain as discrete particles in the dried or cured coating. The voided latex particles are capable of functioning as opacifiers; that is, when added in sufficient amount to a coating composition that would otherwise be transparent when dried, they render the dried coating composition opaque. By the term “opaque”, it is meant that the refractive index of a coating composition has a higher refractive index when the voided latex particles of the present invention are present in a coating composition as compared to the same coating composition not including the voided latex particles of the present invention wherein the refractive index is measured after the coatings are dry to the touch. The term “outer shell polymer” refers to the outer layer of the particle of the present invention after swelling.

The voided latex particles of the invention generally comprise a hollow interior and an outer shell which encloses the hollow interior, although as will be explained subsequently in more detail one or more additional layers may be present between the outer shell and the interior void of each particle. Generally speaking, the voided latex particles may have a diameter of at least 200 nm, at least 250 nm, at least 300 nm, at least 350 nm, or at least 400 nm and a diameter of not more than 1200 nm, not more than 700 nm, not more than 650 nm, not more than 600 nm, not more than 550 nm, or not more than 500 nm. The hollow interior generally has a diameter of at least 100 nm, at least 150 nm, or at least 200 nm, but typically is not more than 600 nm or not more than 500 nm or not more than 400 nm in diameter. The thickness of the layers surrounding the hollow interior, including the outer shell and also any additional layers which may be present, generally is from 30 to 120 nm. Typically, the voided latex particles will be approximately spherical in shape, although oblong, oval, teardrop or other shapes are also possible.

The outer shell is polymeric and may, for example, be comprised of a thermoplastic polymer. The outer shell polymer has a glass transition temperature (Tg) above ambient temperature, typically at least above 45° C., at least 50° C., at least 60° C., at least 70° C., at least 80° C. or at least about 90° C. The Tg of the outer shell polymer may be, for example, from 60° C. to 140° C. Although the outer shell polymer may be a homopolymer, more typically it will be a copolymer comprised of recurring polymerized units of two or more different monomers, especially ethylenically unsaturated monomers such as those capable of being polymerized by free radical polymerization. The outer shell polymer is further characterized by bearing one or more different types of functional groups, particularly reactive, polar, chelating and/or heteroatom-containing functional groups. These functional groups may be varied and chosen as desired to modify certain characteristics of the voided latex particles, such as the wet adhesion, scrub resistance (washability), stain resistance, solvent resistance and block resistance properties of a coating composition which includes the voided latex particles. For example, the functional groups may be selected from 1,3-diketo, amino, ureido and urea functional groups and combinations thereof. Suitable 1,3-diketo functional groups include acetoacetate functional groups, which may correspond to the general structure —OC(═O)CH₂C(═O)CH₃. Suitable amino functional groups include primary, secondary and tertiary amine groups. The amino functional group may be present in the form of a heterocyclic ring. The amino functional group may, for example, be an oxazoline ring. Other types of functional groups useful in the present invention include, for example, hydroxyl (—OH), silane (e.g., trialkoxysilyl, —Si(OH)₃), phosphate (e.g., PO₃H and salts thereof), fluorocarbon (e.g., perfluoroalkyl such as trifluoromethyl), polyether (e.g., polyoxyethylene, polyoxypropylene), and epoxy (e.g., glycidyl). In one embodiment, the functional group contains a Lewis base such as the nitrogen atom of an amine. In another embodiment, the functional group contains a hydroxyl functional group. The functional group may be reactive; for example, the functional group may be capable of reacting as an electrophile or a nucleophile. The functional group, or a combination of functional groups in proximity to each other, may be capable of complexation or chelation.

The functional groups may be introduced into the outer shell polymer by different means. In one embodiment, the functional groups are introduced into the outer shell polymer during formation of the polymer, for example by polymerization of one or more polymerizable monomers bearing the desired functional groups (hereinafter “functionalized monomer”). Such polymerization may be carried out as a copolymerization wherein one or more functionalized monomers are copolymerized with one or more non-functionalized monomers. The monomers having functional groups described herein may be added at any stage in the preparation of the multi-stage emulsion provided that polymers bearing such functional groups at least partially or completely reside in the outer shell polymer of the particles after swelling.

For example, the outer shell polymer may be a copolymer of a vinyl aromatic monomer (e.g., styrene) and a free radical polymerizable ethylenically unsaturated monomer containing a functional group such as a 1,3-diketo, amino, ureido, urea, hydroxyl, silane, fluorocarbon, aldehyde, ketone, phosphate or polyether functional group. The copolymer may contain one or more other additional types of comonomers, such as alkyl (meth)acrylates (e.g., methyl methacrylate). The proportions of different monomers may be varied as may be desired to impart certain characteristics to the resulting outer shell polymer. Typically, the copolymer contains from 0.1 to 10 weight % of free radical polymerizable ethylenically unsaturated monomer(s) containing the functional group(s). Such a copolymer may further comprise 80-99.9 weight % of a vinyl aromatic monomer such as styrene and 0-10 weight % (e.g., 0.1-10 weight %) of an alkyl (meth)acrylate such as methyl methacrylate.

The free radical polymerizable ethylenically unsaturated monomer may contain a (meth)acrylate (i.e., acrylate or methacrylate) group or a (meth)acrylamide (i.e., acrylamide or methacrylamide) group. Such (meth)acrylate and (meth)acrylamide groups are capable of participating in free radical copolymerization with the vinyl aromatic monomer. Allylic groups may also be used to provide a polymerizable site of unsaturation.

Imidazolidinone (meth)acrylic monomers such as 2-(2-oxo-1-imidazolidinyl)ethyl (meth)acrylates and N-(2-(2-oxo-1-imidazolidinyl)ethyl (meth)acrylamides may be utilized as comonomers, for example. Other suitable free radical polymerizable ethylenically unsaturated monomers containing functional groups useful in the practice of the present invention include, without limitation, acetoacetoxy(meth)acrylates (e.g., acetoacetoxyethyl methacrylate, AAEM), allyl acetoacetate, methylolated diacetone (meth)acrylamides, aminoalkyl(meth)acrylates (including dialkyl and monoalkyl aminoethyl(meth)acrylates), and ethylenically unsaturated polymerizable aziridinyl monomers (such as those described, for example, in U.S. Pat. No. 3,719,646, incorporated herein by reference in its entirety for all purposes). Other suitable free radical polymerizable ethylenically unsaturated monomers containing useful functional groups include hydroethylethylene urea methacrylate (HEEUMA) and aminoethylethylene urea methacrylate (AEEUMA). The free radical polymerizable ethylenically unsaturated monomer may contain a plurality of functional groups on each monomer molecule; for example, the monomer may bear two or more urea and/or ureido groups per molecule, such as the compounds described in U.S. Pat. No. 6,166,220 (incorporated herein by reference in its entirety for all purposes). Illustrative examples of particular free radical polymerizable ethylenically unsaturated monomers suitable for use in the present invention as functionalized monomers include, but are not limited to, aminoethyl acrylate and methacrylate, dimethylaminopropylacrylate and methacrylate, 3-dimethylamino-2,2-dimethylpropyl-1-acrylate and methacrylate, 2-N-morpholinoethyl acrylate and methacrylate, 2-N-piperidinoethyl acrylate and methacrylate, N-(3-dimethylaminopropyl)acrylamide and methacrylamide, N-(3-dimethylamino-2,2-dimethylpropyl)acrylamide and methacrylamide, N-dimethylaminomethyl acrylamide and methacrylamide, N-(4-morpholino-methyl)acrylamide and methacrylamide, vinylimidazole, vinylpyrrolidone, N-(2-methacryloyloxyethyl)ethylene urea, N-(2-methacryloxyacetamidoethyl)-N, allylalkyl ethylene urea, N-methacrylamidomethyl urea, N-methacryloyl urea, 2-(1-imidazolyl)ethyl methacrylate, 2-(1-imidazolidin-2-on)ethylmethacrylate, N-(methacrylamido)ethyl urea, glycidyl (meth)acrylates, hydroxyalkyl(meth)acrylates such as 2-hydroxyethyl(meth)acrylates, gamma-(meth)acryloxypropyltrialkoxysilanes, N,N-dimethyl(meth)acrylamides, diacetone(meth)acrylamides, ethylene glycol (meth)acrylate phosphates, polyethylene glycol (meth)acrylates, polyethylene glycol methyl ether (meth)acrylates, diethylene glycol (meth)acrylates and combinations thereof.

In another embodiment of the invention, a precursor polymer is first prepared and then reacted so as to introduce the desired functional groups and thus provide the outer shell polymer. For example, amine functional groups may be introduced to the outer shell polymer by reacting a precursor polymer bearing carboxylic acid groups with an aziridine. In this example, the precursor polymer may be a polymer prepared by polymerizing an ethylenically unsaturated carboxylic acid such as (meth)acrylic acid, optionally together with other monomers such as alkyl (meth)acrylates and/or vinyl aromatic monomers (e.g., styrene).

The voided latex particles of the present invention may be prepared by different methods, including, for example, by processes which utilize multi-stage emulsion polymer particles. The multi-stage emulsion polymer particles may comprise a core comprising a polymer of at least one hydrophilic monoethylenically unsaturated monomer and an outer shell comprising an outer shell polymer bearing functional groups selected from 1,3-diketo, amino, ureido, urea, hydroxyl, epoxy, silane, polyether, fluorocarbon, aldehyde, ketone, acetoacetyl, or phosphate functional groups or combinations thereof. The multi-stage emulsion polymer particles may be contacted with a swelling agent, such as a base, which is capable of swelling the core, particularly in the presence of water.

The swollen core causes the outer shell to expand, such that when the polymer particles are subsequently dried and/or re-acidified the outer shell remains enlarged in volume and a void is created within the particle as a result of the shrinkage of the swollen core. As the swollen core shrinks, it may form a coating on the interior surface of the shell of the particle. The voided latex particles may each contain a single void. However, in other embodiments of the invention, the individual voided latex particles may contain a plurality of voids (e.g., a voided latex particle may contain two or more voids within the particle). The voids may be connected to each other through pores or other passageways. The voids may be substantially spherical in shape, but may adopt other forms such as void channels, interpenetrating networks of void and polymer, or sponge-like structures.

The aforementioned multi-stage emulsion polymer particles may be prepared by sequential emulsion polymerization, using a batch process where the product of one stage is used in the stage that follows. For instance, the product of the core stage may be used to prepare the product of the next stage, be it an outer shell or an intermediate encapsulating polymer stage. Similarly, the shell stage is prepared from the product of the core stage or, when there are one or more encapsulating polymer stages, an intermediate encapsulating polymer stage.

The core component of the multi-stage emulsion polymer particles is generally located at or near the center of such particles. However, in one embodiment, the core may coat and surround a seed which is comprised of a polymer different from the polymer used to prepare the core. In this embodiment, for example, the seed may comprise a polymer which is non-hydrophilic in character; i.e., the seed polymer may be a homopolymer or copolymer of one or more non-ionic monoethylenically unsaturated monomers such as methyl methacrylate. In one embodiment, the seed polymer is a methyl methacrylate homopolymer which is resistant to swelling by the swelling agent used to swell the core. The seed typically has a particle size of from about 30 to about 200 nm or from about 50 to about 100 nm. To form the core, the seed may be coated with another polymer which is comprised of at least one hydrophilic monoethylenically unsaturated monomer, optionally in combination with at least one non-hydrophilic monoethylenically unsaturated monomer such as an alkyl (meth)acrylate and/or a vinyl aromatic monomer. Sufficient hydrophilic monoethylenically unsaturated monomer should be used, however, such that the resulting polymer is capable of being swollen with a swelling agent such as an aqueous base. In one embodiment, for example, the polymer used to coat the seed and provide the core component is a copolymer of methyl methacrylate and methacrylic acid, the methacrylic acid content of the copolymer being about 30 to about 60 weight percent.

The core comprises a hydrophilic component that provides a sufficient degree of swelling for hollow or void formation. In some embodiments, the hydrophilic component is provided in the form of a hydrophilic monomer used to prepare the core polymer (i.e., a polymer used to obtain the core includes polymerized units of a hydrophilic monomer, in an amount effective to render the core polymer hydrophilic). In other embodiments, the hydrophilic component is an additive to the core (for example, the hydrophilic component may be admixed with a non-hydrophilic polymer). In further embodiments, the hydrophilic component is present both as an additive embedded in the core and as a hydrophilic polymer which is part of the core. In some embodiments, the hydrophilic component is an acid-containing monomer or additive, such as a monomer or additive bearing carboxylic acid functional groups.

In some embodiments, one or more of the polymers used to prepare the core may be converted to a swellable component after the polymer has already been prepared. For example, a polymer containing vinyl acetate units may be hydrolyzed to form a core polymer containing sufficient hydroxy groups such that the polymer is swellable.

The hydrophilic component of the core may be provided by polymerization or copolymerization of one or more monoethylenically unsaturated monomers bearing a hydrophilic functional group such as a carboxylic acid group or some other type of ionizable functional group. In some embodiments, such a monoethylenically unsaturated monomer is co-polymerized with at least one nonionic monoethylenically unsaturated monomer.

Examples of hydrophilic monoethylenically unsaturated monomers useful for making the core polymer include monoethylenically unsaturated monomers containing acid-functionality such as monomers containing at least one carboxylic acid group or one phosphoric acid group, including acrylic acid, methacrylic acid, acryloxypropionic acid, (meth)acryloxypropionic acid, itaconic acid, aconitic acid, maleic acid or anhydride, fumaric acid, crotonic acid, monomethyl maleate, monomethyl fumarate, monomethyl itaconate and the like. In certain embodiments, the hydrophilic monoethylenically unsaturated monomer is acrylic acid or methacrylic acid.

Examples of hydrophilic non-polymeric components that may be present in the core include compounds containing one or more carboxylic acid groups such as aliphatic or aromatic monocarboxylic acids and dicarboxylic acids, such as benzoic acid, m-toluic acid, p-chlorobenzoic acid, o-acetoxybenzoic acid, azelaic acid, sebacic acid, octanoic acid, cyclohexanecarboxylic acid, lauric acid and monobutyl phthalate and the like.

The hydrophilic monoethylenically unsaturated monomer may be present in the core polymer in amounts of, as polymerized units, from about 5 to about 80, from about 10 to about 80, from about 20 to about 80, from about 30 to about 70, from about 30 to about 60, from about 40 to about 60, or from about 30 to about 50, percent by weight, based on the weight of core polymer.

The core polymer may additionally contain recurring units derived from non-ionic monomers. Examples of non-ionic monomers that may be present in polymerized form in the swellable core polymer include vinyl aromatic monomers such as styrene, a-methyl styrene, p-methyl styrene, t-butyl styrene, or vinyltoluene, olefms such as ethylene, vinyl acetate, vinyl chloride, vinylidene chloride, (meth)acrylonitrile, (meth)acrylamide, (C₁-C₂₀) alkyl or (C₃-C₂₀) alkenyl esters of (meth)acrylic acid, such as methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, 2-ethyihexyl (meth)acrylate, hydroxyethyl(meth)acrylate, hydroxypropyl(meth)acrylate, benzyl (meth)acrylate, lauryl (meth)acrylate, oleyl (meth)acrylate, palmityl (meth)acrylate, stearyl (meth)acrylate and the like.

The core polymer may further contain polyethylenically unsaturated monomer in amounts, as polymerized units, of 0.1 to 20 percent. Examples of suitable polyethylenically unsaturated monomers include co-monomers containing at least two polymerizable vinylidene groups such as α,β-ethylenically unsaturated monocarboxylic acid esters of polyhydric alcohols containing 2-6 ester groups. Such co-monomers include alkylene glycol diacrylates and dimethacrylates, such as for example, ethylene glycol diacrylate, ethylene glycol dimethacrylate, 1,3-butylene glycol diacrylate, 1,4-butylene glycol diacrylate propylene glycol diacrylate and triethylene glycol dimethylacrylate; 1,3-glycerol dimethacrylate; 1,1,1-trimethylol propane dimethacrylate; 1,1,1-trimethylol ethane diacrylate; pentaerythritol trimethacrylate; 1,2,6-hexane triacrylate; sorbitol pentamethacrylate; methylene bis-acrylamide, methylene bis-methacrylamide, divinyl benzene, vinyl methacrylate, vinyl crotonate, vinyl acrylate, vinyl acetylene, trivinyl benzene, triallyl cyanurate, divinyl acetylene, divinyl ethane, divinyl sulfide, divinyl ether, divinyl sulfone, diallyl cyanamide, ethylene glycol divinyl ether, diallyl phthalate, divinyl dimethyl silane, glycerol trivinyl ether, divinyl adipate; dicyclopentenyl (meth)acrylates; dicyclopentenyloxy (meth)acrylates; unsaturated esters of glycol monodicyclopentenyl ethers; allyl esters of α,β-unsaturated mono- and dicarboxylic acids having terminal ethylenic unsaturation including allyl methacrylate, allyl acrylate, diallyl maleate, diallyl fumarate, diallyl itaconate and the like.

The multi-stage emulsion polymer particles may contain one or more intermediate encapsulating polymer layers. The intermediate encapsulating polymers partially or fully encapsulate the core. Each encapsulating polymer layer may be partially or fully encapsulated by another encapsulating polymer layer. Each encapsulating polymer layer may be prepared by conducting an emulsion polymerization in the presence of the core or a core encapsulated by one or more encapsulating polymers. The intermediate encapsulating polymer layer may function as a compatiblizing layer, sometimes referred to as a tie or tie coat layer, between other layers of the multi-stage emulsion polymer particles; for example, an intermediate encapsulating polymer layer may help adhere the outer shell to the core. An intermediate encapsulating polymer layer may also serve to modify certain characteristics of the final voided latex particles.

At least one intermediate encapsulating polymer may contain, as polymerized units, one or more hydrophilic monoethylenically unsaturated monomers and one or more nonionic monoethylenically unsaturated monomers. The hydrophilic monoethylenically unsaturated monomers and the nonionic monoethylenically unsaturated monomers useful for making the core are also useful for making such an intermediate encapsulating polymer. Generally, however, the intermediate encapsulating polymer contains a lower proportion of hydrophilic monomer than the core polymer, such that the intermediate incapsulating polymer swells less when contacted with the swelling agent. Other intermediate encapsulating polymers may contain, as polymerized units, non-ionic monoethylenically unsaturated monomer and little or no (e.g., less than 5 weight %) hydrophilic monoethylenically unsaturated monomer. Intermediate encapsulating polymers may further include crosslinking agents such as alkylene glycol diacrylates and dimethacrylates, such as for example, ethylene glycol diacrylate, ethylene glycol dimethacrylate, 1,3-butylene glycol diacrylate, 1,4-butylene glycol diacrylate propylene glycol diacrylate and triethylene glycol dimethylacrylate; 1,3-glycerol dimethacrylate; 1,1,1-trimethylol propane dimethacrylate; 1,1,1-trimethylol ethane diacrylate; pentaerythritol trimethacrylate; 1,2,6-hexane triacrylate; sorbitol pentamethacrylate; methylene bis-acrylamide, methylene bis-methacrylamide, divinyl benzene, vinyl methacrylate, vinyl crotonate, vinyl acrylate, vinyl acetylene, trivinyl benzene, triallyl cyanurate, divinyl acetylene, divinyl ethane, divinyl sulfide, divinyl ether, divinyl sulfone, diallyl cyanamide, ethylene glycol divinyl ether, diallyl phthalate, divinyl dimethyl silane, glycerol trivinyl ether, divinyl adipate; dicyclopentenyl (meth)acrylates; dicyclopentenyloxy (meth)acrylates; unsaturated esters of glycol monodicyclopentenyl ethers; allyl esters of α,β-unsaturated mono- and dicarboxylic acids having terminal ethylenic unsaturation including allyl methacrylate, allyl acrylate, diallyl maleate, diallyl fumarate, diallyl itaconate and the like.

The free radical initiators suitable for the polymerization of the monomers used to prepare the multi-stage emulsion polymer particles may be any water soluble initiator suitable for aqueous emulsion polymerization. Examples of free radical initiators suitable for the preparation of the multi-stage emulsion polymer particles of the present application include hydrogen peroxide, tert-butyl peroxide, alkali metal persulfates such as sodium, potassium and lithium persulfate, ammonium persulfate, and mixtures of such initiators with a reducing agent. The amount of initiator may be, for example, from 0.01 to 3 percent by weight, based on the total amount of monomer.

In some embodiments, a redox polymerization initiator system is used. In a redox free radical initiation system, a reducing agent may be used in conjunction with an oxidant. Reducing agents suitable for the aqueous emulsion polymerization include sulfites (e.g., alkali metal metabisulfite, hydrosulfite and hyposulfite). In some embodiments, sugars (such as alkali metal (iso)ascorbate salt, ascorbic acid and isoascorbic acid) might also be a suitable reducing agent for the aqueous emulsion polymerization.

In a redox system, the amount of reducing agent may be, for example, from 0.01 to 3 percent by weight based on the total amount of monomer.

Oxidizing agents include, for example, for example, hydrogen peroxide and ammonium or alkali metal persulfates, perborates, peracetates, peroxides, and percarbonates and a water-insoluble oxidizing agent such as, for example, benzoyl peroxide, lauryl peroxide, t-butyl peroxide, t-butyl hydroperoxide, 2,2′-azobisisobutyronitrile, t-amyl hydroperoxide, t-butyl peroxyneodecanoate, and t-butyl peroxypivalate. The amount of oxidizing agent may be, for example, from 0.01 to 3 percent by weight, based on the total amount of monomer.

The free radical polymerization temperature typically is in the range of about 10° C. to 100° C. In the case of the persulfate systems, the temperature may be in the range of about 60° C. to about 100° C. In the redox system, the temperature may be in the range of about 30° C. to about 100° C., in the range of about 30° C. to about 60° C., or in the range of about 30° C. to about 45° C. The type and amount of initiator may be the same or different in the various stages of the multi-stage polymerization.

One or more nonionic or ionic (e.g., cationic, anionic) emulsifiers, or surfactants, may be used, either alone or together, during polymerization in order to emulsify the monomers and/or to keep the resulting polymer particles in dispersed or emulsified form. Examples of suitable nonionic emulsifiers include tert-octylphenoxyethylpoly(39)-ethoxyethanol, dodecyloxypoly(10)ethoxyethanol, nonylphenoxyethyl-poly(40)ethoxyethanol, polyethylene glycol 2000 monooleate, ethoxylated castor oil, fluorinated alkyl esters and alkoxylates, polyoxyethylene (20) sorbitan monolaurate, sucrose monococoate, di(2-butyl)phenoxypoly(20)ethoxyethanol, hydroxyethylcellulosepolybutyl acrylate graft copolymer, dimethyl silicone polyalkylene oxide graft copolymer, poly(ethylene oxide)poly(butyl acrylate) block copolymer, block copolymers of propylene oxide and ethylene oxide, 2,4,7,9-tetramethyl-5-decyne-4,7-diol ethoxylated with 30 moles of ethylene oxide, N-polyoxyethylene(20)lauramide, N-lauryl-N-polyoxyethylene(3)amine and poly(10)ethylene glycol dodecyl thioether. Examples of suitable ionic emulsifiers include sodium lauryl sulfate, sodium dodecylbenzenesulfonate, potassium stearate, sodium dioctyl sulfosuccinate, sodium dodecyldiphenyloxide disulfonate, nonylphenoxyethylpoly(l)ethoxyethyl sulfate ammonium salt, sodium styrene sulfonate, sodium dodecyl allyl sulfosuccinate, palmitic acid, palmitoleic acid, stearic acid, oleic acid, linoleic acid, linolenic acid, mixtures of fatty acids (e.g., linseed oil fatty acid), sodium or ammonium salts of phosphate esters of ethoxylated nonylphenol, sodium octoxynol-3-sulfonate, sodium cocoyl sarcocinate, sodium 1-alkoxy-2-hydroxypropyl sulfonate, sodium α-olefin (C₁₄-C₁₆)sulfonate, sulfates of hydroxyalkanols, tetrasodium N-(1,2-dicarboxy ethyl)-N-octadecylsulfosuccinamate, disodium N-octadecylsulfosuccinamate, disodium alkylamido polyethoxy sulfosuccinate, disodium ethoxylated nonylphenol half ester of sulfosuccinic acid and the sodium salt of tert-octylphenoxyethoxypoly(39)ethoxyethyl sulfate.

The one or more emulsifiers or surfactants are generally used at a level of from zero to 3 percent based on the weight of the monomers. The one or more emulsifiers or surfactants can be added prior to the addition of any monomer charge, during the addition of a monomer charge or a combination thereof.

Suitable swelling agents are generally bases, including volatile bases such as ammonia, ammonium hydroxide, and volatile lower aliphatic amines, such as morpholine, trimethylamine, and triethylamine, and the like. Fixed or permanent bases such as sodium hydroxide, potassium hydroxide, lithium hydroxide, zinc ammonium complex, copper ammonium complex, silver ammonium complex, strontium hydroxide, barium hydroxide and the like may also be used. Solvents, such as, for example, ethanol, hexanol, octanol, and Texanol® solvent and those described in U.S. Pat. No. 4,594,363, may be added to aid in fixed or permanent base penetration. In some embodiments, the swelling agent is ammonia or ammonium hydroxide. The swelling agent may be in the form of an aqueous liquid or a gaseous medium containing a volatile base. The compositions of the outer shell and any intermediate encapsulating layers may be selected so as to be permeable to the swelling agent at ambient temperature or at a moderately elevated temperature. In one embodiment, the swelling agent is contacted with the multi-stage emulsion polymer particles at a temperature somewhat less than the glass transition temperature of the outer shell polymer. For example, the contacting temperature may be 5 to 20° C. less than the outer shell polymer Tg.

The hydrophilic component of the core swells when the multi-stage emulsion polymer particles are subjected to a basic swelling agent that permeates the outer shell of the multi-stage emulsion polymer particles (and any intermediate encapsulating layers, if present). In one embodiment of the invention, the hydrophilic component of the core is acidic (having a pH less than 6). Treatment with a basic swelling agent neutralizes the acidity and raises the pH of the hydrophilic component greater than 6, or at least about 7, or to at least about 8, or at least about 9, or at least about 10, or to at least about 13, thereby causing swelling by hydration of the hydrophilic component of the core. The swelling, or expansion, of the core may involve partial merging of the outer periphery of the core into the pores of the inner periphery of the layer immediately adjacent to the core (such as the outer shell or an intermediate encapsulating shell) and also partial enlargement or bulging of such adjacent layer and the entire particle overall. Swelling may be carried out before or after the outer shell is formed or before the outer shell is completely formed.

The weight ratio of the core to the outer shell may generally, for example, be in the range of from 1:5 to 1:20 (e.g., from 1:8 to 1:15). To decrease the dry density of the final voided latex particles, the amount of outer shell relative to the amount of core should generally be decreased; however, sufficient outer shell should be present such that the core is still encapsulated.

Methods previously described in the art for producing voided latex particles may be adapted for use in the present invention, provided the composition of the polymer utilized to form the outer shell of such particles is modified to provide a functionalized polymer in accordance with the invention (e.g., an outer shell polymer bearing functional groups selected from 1,3-diketo, amino, ureido and urea functional groups or combinations thereof, and/or any of the other functional groups described herein). Methods for obtaining voided latex particles are described, for example, in U.S. Pat. Nos. 4,427,836; 4,468,498; 4,594,363; 4,880,842; 4,920,160; 4,985,469; 5,216,044; 5,229,209; and 5,273,824, each of which is incorporated herein by reference in its entirety for all purposes. For example, particles in accordance with the present invention may be made by incorporating the functional monomers described herein into the outer shell of the particles described in the following examples: (1) examples 0-14 of U.S. Pat. No. 4,427,836, (2) examples 0-12 of U.S. Pat. No. 4,468,498, (3) examples 1-4 of U.S. Pat. No. 4,594,363, (4) examples I-IX of U.S. Pat. No. 4,880,842, (5) examples 1-13 of U.S. Pat. No. 4,920,160, (6) examples 1-7 of U.S. Pat. No. 4,985,469, (7) examples 1-7 of U.S. Pat. No. 5,216,044, (8) examples 1-8 of U.S. Pat. No. 5,229,209, and (9) examples 1-50 of U.S. Pat. No. 5,273,824.

FIG. 1 illustrates in schematic form an exemplary process which can be used to prepare multi-stage emulsion polymer particles and voided latex particles in accordance with the invention. In Step 1, methyl methacrylate (MMA) is homopolymerized to form seed 1 as a small particle comprised of polymethyl methacrylate. Seed 1 is coated with a layer of methyl methacrylate/methacrylic acid copolymer by copolymerization of methyl methacrylate (MMA) monomer and methacrylic acid (MAA) monomer to provide core 2 (Step 2). In Step 3, encapsulating polymer layer 3 is formed by copolymerization of styrene (S) monomer and methyl methacrylate (MMA) monomer. In this embodiment, encapsulating polymer layer 3 is capable of functioning as a tie-coat between core 2 and outer shell 4, which is formed in Step 4 by copolymerization of styrene (S) monomer and a functionalized monomer (FM) such as an imidazolidinone (meth)acrylic monomer. In other embodiments, encapsulating polymer layer 3 may be omitted. More than one encapsulating polymer layer between core layer 2 and outer shell 4 may be present, if so desired. A multi-stage emulsion polymer particle 7 is obtained following Step 4. Multi-stage emulsion polymer particle 7 is contacted with aqueous ammonium hydroxide in Step 5. The ammonium hydroxide acts as a swelling agent, wherein the carboxylic acid functional groups of the MMA/MAA copolymer of core 2 are at least partially neutralized and core 2 swells in volume as a result of absorption of water by neutralized core 2. The volume increase of core 2 pushes encapsulating polymer layer 3 and outer shell 4 outwardly and the overall diameter of the multi-stage emulsion polymer particle increases. Drying the particles in Step 6 provides voided latex particle 6. Voided latex particle 6 is characterized by having an outer shell 4 surrounding hollow interior 5, wherein the outer shell 4 is comprised of a polymer bearing functional groups such as ureido functional groups derived from the functionalized monomer. Residues of seed 1 and core 2 may still be present within hollow interior 5.

The voided latex particles in accordance with the present invention are useful in coating compositions, such as aqueous-based paint and paper coatings. Voided latex particles in accordance with this invention may be capable of imparting improved gloss, brightness and opacity to paper coating formulations to which they are added. Also, voided latex particles in accordance with this invention may be capable of imparting opacity to aqueous coating compositions, such as paints, to which they are added. In addition, the wet adhesion of coating compositions can be improved by including voided latex particles in accordance with this invention, especially where the outer shell polymer contains functional groups selected from 1,3-diketo, amino, ureido and urea functional groups.

For example, a coating composition may contain, in addition to water, voided latex particles in accordance with this invention, one or more film-forming latex polymers (e.g., an acrylic (A/A) latex and/or a vinyl acrylic (V/A) latex), and, if so desired, any of the additives or other components typically employed in such latex coating compositions such as coalescing solvents, biocides, pigments, fillers, opacifying agents other than the voided latex particles (e.g., titanium dioxide, CaCO₃), thickeners, leveling agents, pH adjusting agents, surfactants, antifreeze agents and the like. Voided latex particles may be present in such coating compositions at levels of, for example, 0.5 to 10 weight percent.

The film-forming latex polymer used in combination with the voided latex particles of the present invention may also be selected such that it also contains functional groups which help to modify or enhance certain characteristics of the coating composition, such as wet adhesion, scrub resistance, solvent resistance, stain resistance or the like. For example, the film-forming latex polymer may be a polymer prepared by polymerization of a so-called wet adhesion monomer, optionally in combination with one or more other types of comonomers. The wet adhesion monomer may be, for instance, an ethylenically unsaturated compound bearing a urea, ureido, 1,3-diketo, amino or other such functional group. Such functionalized film-forming latex polymers are well known in the art and are described, for example, in U.S. Pat. Nos. 3,935,151; 3,719,646; 4,302,375; 4,340,743; 4,319,032; 4,429,095; 4,632,957; 4,783,539; 4,880,931; 4,882,873; 5,399,706; 5,496,907; and 6,166,220, each of which is incorporated herein by reference in its entirety for all purposes.

In one embodiment of the invention, a film-forming latex polymer is selected for use in a coating composition in combination with the non-film-forming voided latex particles described herein wherein the film-forming latex polymer contains functional groups capable of interacting with the functional groups present in the outer shell of the non-film-forming voided latex particles so as to provide a crosslinking effect. Such crosslinking effect may result when the coating composition is applied to a substrate surface and dried, for example. This interaction typically takes place through chemical reaction between the two types of functional groups resulting in the formation of covalent bonds, although the interaction could alternatively be the result of a non-covalent association such as complexation or formation of a salt. The opacity and solvent resistance of the coating may, for example, be enhanced through the use of such functionalized film-forming latex polymer and functionalized non-film-forming voided latex particles in combination with each other.

Examples of pairs of functional groups capable of interacting with each other are as follows. Functional Group A may be on the non-film-forming voided latex particles (as part of the outer shell polymer) and Functional Group B may be present in the film-forming latex polymer component. Alternatively, Functional Group A may be present in the film-forming polymer and Functional Group B may be present in the outer shell of the non-film-forming voided latex particles.

Functional Group Pair Functional Group A Functional Group B 1 Carbonyl Hydrazide 2 Epoxy Amine 3 Oxazoline Aldehyde 4 AAEM (acetoacetyl Amine ethyl methacrylate

In yet another embodiment of the invention, the coating composition is formulated so as to contain one or more non-polymeric compounds bearing two or more functional groups per molecule capable of interacting with the functional groups present in the outer shell of the non-film-forming voided latex particles. Such non-polymeric compounds thus also may function as crosslinking agents. For example, where the outer shell contains acetoacetate groups, a non-polymeric compound containing a plurality of primary amine groups on each molecule may be employed.

In still another embodiment, the functional groups present in the outer shell of the non-film-forming voided latex particles are selected so as to be capable of condensing with each other thereby forming linkages between different particles. For instance, the outer shell may bear —Si(OH)₃ functional groups which may undergo a dehydration reaction to form a siloxane linkage (e.g., —Si(OH)₂—O—Si(OH)₂—).

EXAMPLES

The binders (film forming latexes) used were commercial samples. The A/A latex (ENCOR (previously known as UCAR) Latex 634, supplied by Arkema Inc.) and the V/A latex (ENCOR (previoiusly known as UCAR) Latex 300, also supplied by Arkema Inc.) have identical glass transition temperatures (T_(g)) of 4° C. and can be formulated to form a film at room temperature without the need for coalescing solvents.

The opacifiers were evaluated in the paint formulations outlined in Tables 3 and 4. The paints were all formulated at 35% pigment volume concentration (PVC) and 40.0% volume solids. All the paints were tinted with 1.25 ozs/gallon of Colortrend® 888, Colorant B (lamp black).

The paints outlined in Table 1 contained 50 to 200 lbs/100 gallons TiO₂ with the remaining “pigment” volume being made up with opacifier, which resulted in opacifier use levels ranging from 40 to 60 dry lbs/100 gallons. This is above current standard opacifier usage, which typically varies from 10 to 30 dry lbs/100 gallons. V/A-A/A blend ratios of 100-0, 92.5-7.5, and 85-15% were explored. In Tables 1 and 2, opacifier Sample A is the Control, wherein the outer shell of the voided latex particles is a styrene homopolymer. The other opacifiers tested, Sample B and Sample C, were voided latex particles in accordance with the invention containing outer shells comprised of styrene/2-(2-oxo-1-imidazolidinyl)ethyl methacrylate copolymer containing 2 phm and 4 phm of polymerized 2-(2-oxo-1-imidazolidinyl)ethyl methacrylate (hereafter referred to as “functionalized monomer” or “FM”) respectively.

TABLE 1 Ingredient Form 1 Form 2 Form 3 Form 4 Form 5 Form 6 Form 7 Form 8 Form 9 Ti-Pure R-746 65.4 65.4 65.4 261.4 261.4 261.4 163.4 163.4 163.4 Water 180.7 180.7 180.7 167.5 167.5 167.5 171.4 171.4 171.4 NH4OH, 28% 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 Sample A Opacifier 201.4 0.0 0.0 128.8 0.0 0.0 165.1 0.0 0.0 Sample B 0.0 201.4 0.0 0.0 128.8 0.0 0.0 165.1 0.0 Sample C 0.0 0.0 201.4 0.0 0.0 128.8 0.0 0.0 165.1 UCAR 300 448.3 448.3 448.3 448.2 448.2 448.2 413.7 413.7 413.7 UCAR 634 0.0 0.0 0.0 0.0 0.0 0.0 36.8 36.8 36.8 Water Slurried 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 Tamol 1124 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 Omyacarb UF 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 Polyphobe TR-115 6.3 6.3 6.3 6.3 6.3 6.3 5.9 5.9 5.9 Polyphobe TR-117 6.3 6.3 6.3 6.3 6.3 6.3 6.6 6.6 6.6 Total 909.7 909.7 909.7 1019.9 1019.9 1019.9 964.4 964.4 964.4 PVC 35.0 35.0 35.0 35.0 35.0 35.0 35.0 35.0 35.0 wt % 39.7 39.7 39.7 48.0 48.0 48.0 43.8 43.8 43.8 vol % 40.0 40.0 40.0 40.0 40.0 40.0 40.0 40.0 40.0 Density, lbs/gallon 9.10 9.10 9.10 10.25 10.25 10.25 9.67 9.67 9.67 Volume, gallons 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 Ingredient Form 10 Form 11 Form 12 Form 13 Form 14 Form 15 Ti-Pure R-746 65.4 65.4 65.4 261.4 261.4 261.4 Water 175.3 175.3 175.3 162.1 162.1 162.1 NH4OH, 28% 1.5 1.5 1.5 1.5 1.5 1.5 Sample A Opacifier 201.4 0.0 0.0 128.8 0.0 0.0 Sample B 0.0 201.4 0.0 0.0 128.8 0.0 Sample C 0.0 0.0 201.4 0.0 0.0 128.8 UCAR 300 379.3 379.3 379.3 379.1 379.1 379.1 UCAR 634 73.6 73.6 73.6 73.6 73.6 73.6 Water Slurried 0.0 0.0 0.0 0.0 0.0 0.0 Tamol 1124 0.0 0.0 0.0 0.0 0.0 0.0 Omyacarb UF 0.0 0.0 0.0 0.0 0.0 0.0 Polyphobe TR-115 5.6 5.6 5.6 5.5 5.5 5.5 Polyphobe TR-117 6.9 6.9 6.9 7.0 7.0 7.0 Total 909.0 909.0 909.0 1019.0 1019.0 1019.0 PVC 35.0 35.0 35.0 35.0 35.0 35.0 wt % 39.6 39.6 39.6 47.9 47.9 47.9 vol % 40.0 40.0 40.0 40.0 40.0 40.0 Density, lbs/gallon 9.09 9.09 9.09 10.24 10.24 10.24 Volume, gallons 100.0 100.0 100.0 100.0 100.0 100.0

Additional paints were prepared to explore coating performance at lower opacifier loadings. The paints outlined in Table 2 were also prepared with 50 to 200 lbs/100 gallons TiO₂ with the remaining “pigment” volume being made up with either opacifier or CaCO₃, which resulted in opacifier use levels ranging from 0 to 60 dry lbs/100 gallons.

TABLE 2 Ingredient Form 1 Form 2 Form 3 Form 4 Form 5 Form 6 Form 7 Form 8 Form 9 Form 10 Form 11 Ti-Pure R-746 65.4 261.4 65.4 261.4 163.4 163.4 65.4 163.4 163.4 261.4 163.4 Water 135.0 138.5 180.7 167.5 155.4 136.8 157.9 151.2 159.6 153.0 174.1 NH4OH, 28% 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 Sample A Opacifier 0.0 0.0 201.4 128.8 82.5 0.0 100.7 64.4 100.7 64.4 165.1 Sample B 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 Sample C 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 UCAR 300 448.0 448.0 448.3 448.2 448.1 448.0 448.2 448.1 448.2 448.1 448.3 UCAR 634 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 Water Slurried 111.6 71.2 0.0 0.0 45.7 91.4 55.8 55.8 35.6 35.6 0.0 Tamol 1124 27.9 17.8 0.0 0.0 11.4 22.9 14.0 14.0 8.9 8.9 0.0 Omyacarb UF 279.0 178.0 0.0 0.0 114.3 228.5 139.5 139.5 89.0 89.0 0.0 Polyphobe TR-115 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 Polyphobe TR-117 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 6.3 Total 1080.9 1128.9 909.7 1019.9 1034.8 1104.9 995.3 1050.4 1019.3 1074.4 964.8 PVC 35.0 35.0 35.0 35.0 35.0 35.0 35.0 35.0 35.0 35.0 35.0 wt % 53.7 55.8 39.7 48.0 49.3 54.8 46.7 50.9 47.8 51.9 43.9 vol % 40.0 40.0 40.0 40.0 40.0 40.0 40.0 40.0 40.0 40.0 40.0 Density, lbs/gallon 10.8 11.3 9.10 10.25 10.4 11.1 10.0 10.5 10.2 10.8 9.7 Volume, gallons 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0

Wet adhesion refers to the ability of a latex paint to adhere to a substrate under wet conditions. Poor wet adhesion can lead to blistering, peeling, flaking and chipping when the coating is exposed to periods of precipitation and/or temperature-humidity cycles.

The wet adhesion test used herein measures the adhesion of a coating under wet conditions to an aged alkyd substrate. The gloss alkyd panels were prepared by casting a 7-mil film of Glidden Glid-Guard® 4554 gloss alkyd paint onto a Leneta scrub chart and allowing it to cure for 3 to 6 weeks at 25° C. and 50% relative humidity. The test and control paints were drawn down in parallel on the same alkyd panel with a 7-mil Dow bar. After the panels were dried for 24 hours at 25° C. and 50% relative humidity, the films were crosshatched through to the gloss alkyd substrate layer. The test panels were then soaked in water for 30 minutes. Size and density of blisters were noted. Before scrubbing, 20 mL of 50% Lava® soap solution and 5 mL of water were added to the paint panels on the scrub machine. The reported results include the number of cycles at which initial failures were observed and the percent film remaining after 500 cycles.

FIG. 2 illustrates the impact of A/A latex modification, voided latex particle opacifier level, and functionalized monomer content of the outer shells of the voided latex particles on wet adhesion to a gloss alkyd substrate. The paints modified with 7.5% A/A latex and voided latex particles in accordance with the invention (where the outer shell comprised a functionalized polystyrene, where in functionalized monomer content was 2 or 4 phm) had some degree of failure but likely represent the minimum level required for acceptable performance. By contrast, paints modified with 15% A/A latex and a conventional voided latex particle opacifier (containing a styrene homopolymer outer shell) did not achieve adequate wet adhesion performance. 

The invention claimed is:
 1. A voided latex particle comprising a hollow interior and an outer shell, wherein the outer shell is comprised of an outer shell copolymer having a Tg above 45° C. and bearing 0.5 to 5 weight % of one or more ureido functional groups, wherein the outer shell copolymer is a copolymer of a vinyl aromatic monomer and a free radical polymerizable ethylenically unsaturated monomer containing said ureido functional group(s), the copolymer comprising 0.1 to 10 weight % of the free radical polymerizable ethylenically unsaturated monomer containing said functional groups, wherein the voided latex particle is an opacifier which is opaque and non-film-forming at temperatures at or above 15° C., and at or below 45° C., and wherein only the outer shell of said voided latex particle is functionalized with said one or more ureido functional groups.
 2. The voided latex particle of claim 1, wherein the vinyl aromatic monomer is styrene.
 3. The voided latex particle of claim 1, wherein the free radical polymerizable ethylenically unsaturated monomer contains a (meth)acrylate or (meth)acrylamide group.
 4. The voided latex particle of claim 1, wherein the free radical polymerizable ethylenically unsaturated monomer is an imidazolidinone (meth)acrylic monomer.
 5. The voided latex particle of claim 1, wherein the free radical polymerizable ethylenically unsaturated monomer is selected from the group consisting of 2-(2-oxo-1- imidazolidinyl)ethyl (meth)acrylates and N-(2-(2-oxo-1-imidazolidinyl)ethyl (meth)acrylamides.
 6. The voided latex particle of claim 1, wherein the outer shell polymer is a copolymer of a vinyl aromatic monomer and a free radical polymerizable ethylenically unsaturated monomer selected from the group consisting of acetoacetoxy(meth)acrylates, allyl acetoacetate, methylolated diacetone (meth)acrylamides, aminoalkyl(meth)acrylates, and ethylenically unsaturated polymerizable aziridinyl monomers, and optionally comonomer selected from the group consisting of alkyl(meth)acrylates, (meth)acrylamides, and imidazolidinone (meth)acrylics.
 7. The voided latex particle of claim 1, wherein the functional groups are introduced to the outer shell polymer by polymerization of one or monomers bearing the functional groups.
 8. The voided latex particle of claim 1, wherein the functional groups are introduced to the outer shell polymer by reacting a precursor polymer with a functionalization agent capable of forming the functional groups.
 9. The voided latex particles of claim 1 which are capable of providing opacity to an aqueous coating composition comprising film-forming acrylic and/or vinyl acrylic latex polymers and said voided latex particles, when said voided latex particles are present in said coating composition at from 0.5 to 10 weight % based on the total weight of said coating composition.
 10. The voided latex particle of claim 1, wherein the voided latex particle further comprises at least one intermediate encapsulating polymer between the hollow interior and the outer shell.
 11. The voided latex particle of claim 10, wherein the intermediate encapsulating polymer comprises at least one non-ionic monoethylenically unsaturated monomer and at least one crosslinking agent.
 12. The voided latex particle of claim 1, wherein the outer shell polymer has a glass transition temperature of at least 60° C.
 13. A coating composition comprising the voided latex particles in accordance with claim
 1. 14. The coating composition of claim 13, further comprising at least one non-polymeric compound bearing two or more functional groups per molecule capable of interacting with functional groups present in the outer shell polymer.
 15. The coating composition of claim 13, further comprising film-forming latex particles.
 16. The coating composition of claim 15, wherein at least a portion of the film-forming latex particles bear functional groups capable of interacting with the functional groups present in the outer shell polymer.
 17. The coating composition of claim 15, wherein said latex is an acrylic or vinyl acrylic latex.
 18. A paint comprising the coating composition of claim
 15. 19. The paint composition of claim 18, wherein said latex is an acrylic, styrene acrylic or vinyl acrylic latex.
 20. The paint composition of claim 18, further comprising one or more of coalescing solvents, biocides, pigments, fillers, titanium dioxide, calcium carbonate, thickeners, leveling agents, pH adjusting agents, surfactants, or antifreeze agents.
 21. The paint composition of claim 20, wherein said voided latex particles comprise 0.5 to 10 weight % of the paint.
 22. A process for forming the voided latex particles of claim 1, wherein the process comprises contacting multi-stage emulsion polymer particles comprising a core and an outer shell with a swelling agent, wherein: the core comprises a hydrophilic component; the outer shell comprises an outer shell copolymer having a Tg of above 45° C. and bearing one or more ureido functional groups; and the swelling agent is capable of swelling the core.
 23. The process of claim 22, wherein the free radical polymerizable ethylenically unsaturated monomer contains a (meth)acrylate or (meth)acrylamide group.
 24. The process of claim 22, wherein the free radical polymerizable ethylenically unsaturated monomer is an imidazolidinone (meth)acrylic monomer.
 25. The process of claim 22, wherein the free radical polymerizable ethylenically unsaturated monomer is selected from the group consisting of 2-(2-oxo-1- imidazolidinyl)ethyl (meth)acrylates and N-(2-(2-oxo-1-imidazolidinyl)ethyl (meth)acrylamides.
 26. The process of claim 22, wherein the functional groups are introduced to the outer shell polymer by polymerization of one or monomers bearing the functional groups.
 27. The process of claim 22, wherein the multi-stage emulsion polymer particles further comprise at least one intermediate encapsulating polymer comprised of at least one non-ionic monoethylenically unsaturated monomer and at least one hydrophilic monoethylenically unsaturated monomer. 